ABSTRACT

Composite resin materials are most widely used in dentistry today, to fill anterior and posterior teeth. The properties of composite resin are physical properties, mechanical properties, and chemical properties. The properties of composite resin can be affected by low pH (acid). The effect of acidic pH can cause matrix degradation and erosion of composite resin, thus affecting compressive strength, surface hardness, and wear rates. Various previous studies have proven the effect of acidic pH on the mechanical properties of composite resin. The purpose of writing this literature study is to determine how acidic pH affects the mechanical properties of composite resin on compressive strength, surface hardness, and wear rates of composite resin. The effect of acidic pH can cause erosion, matrix separation or hydrolytic degradation of particles/matrix. Acidic pH causes composite resin to erode, which will affect the surface and reduce hardness. Matrix degradation is the breaking of the methacrylate group in Bis-GMA because the composite resin polymer contains unstable bonds so that the matrix is increasingly broken down resulting in decreased compressive strength⁴. As dentists, we should take an important role in choosing composite resin materials used as filling materials.

Keywords: Composite Resin, Mechanical Properties of Composite Resin, Acid pH

ABSTRAK

Bahan resin komposit paling banyak digunakan dibidang kedokteran gigi saat ini, untuk menumpat gigi anterior dan gigi posterior. Sifat Resin komposit yang dimiliki yaitu sifat fisik, sifat mekanik, dan sifat kimiawi. Sifat – sifat  resin komposit dapat dipengaruhi oleh pH rendah (asam).  Pengaruh pH asam dapat mengakibatkan degradasi matriks dan erosi pada resin komposit sehingga mempengaruhi kekuatan tekan, kekerasan permukaan, dan ketahanan terhadap Aus (Wear rates). Berbagai penelitian terdahulu membuktikan adanya pengaruh pH Asam terhadap sifat mekanik resin komposit. Tujuan penulisan studi pustaka ini adalah untuk mengetahui bagaiamana pengaruh pH asam terhadap sifat mekanik resin komposit pada kekuatan tekan, kekerasan permukaan, dan ketahanan terhadap Aus (Wear rates) resin komposit. Efek  pH asam dapat menyebabkan erosi, pemisahan matriks atau degradasi hidrolitik partikel/matriks. pH asam menyebabkan resin komposit tererosi maka akan mempengaruhi permukaan dan menurunkan kekerasan. Degradasi matriks merupakan terputusnya gugus metakrilat pada Bis-GMA karena polimer resin komposit mengandung ikatan yang tidak stabil sehingga matriks semakin terurai mengakibatkan  kekuatan tekan menurun.  Sebagai dokter gigi, kita hendaknya mengambil peran penting dalam memilih bahan resin komposit yang digunakan sebagai bahan tumpatan.

Kata Kunci: Resin Komposit, Sifat Mekanik Resin Komposit, Ph Asam

Abuelenain, D., Neel, E. A. A. & Aldharrab, A. (2015).Mechanical Properties Of Different Commercially Available Dental Composites. Austin J. Dent. 2, 03

Ansuj, M. D. F., Santos, I. S. Dos, Marquezan, M., Durand, L. B. & Pozzobon, R. T. (2016).Evaluation Of The Surface Roughness Of A Nanofilled Composite Resin Submitted To Different Smoothing And Finishing Techniques. Rev. Odontol. Da Unesp 45, 110–114

Anusavice, K. J., Shen, C., & Rawls, H. R. (Eds. ). (2014).Phillips´Sciencie Of Dental Materials. Paper Knowledge . Toward A Media History Of Documents

Claudia., F. (2021).Pengaruh Perendaman Jus Jeruk Terhadap Kekuatan Tekan Glass Ionomer Cement Dan Resin Modified Glass Ionomer Cementpengaruh Perendaman Jus Jeruk Terhadap Kekuatan Tekan Glass Ionomer Cement Dan Resin Modified Glass Ionomer Cement (Doctoral Dissertation, Un. 1–9

Et.Al, K. (2014). In Vitro Evaluation Of The Compressive Strength Of Microhybrid And Nanocomposites. Ohdm 13, 1–6

Ilday, N., Bayindir, Y. Z. & Erdem, V. (2010).Effect Of Three Different Acidic Beverages On Surface Characteristics Of Composite Resin Restorative Materials. Mater. Res. Innov. 14, 385–391

Imansari. (2018).Pengaruh Lama Perendaman Minuman Berkarbonasi Terhadap Penurunan Kekerasan Resin Komposit Nanofiller. 3, 91–102

Kafalia, R. F., Firdausy, M. D. & Nurhapsari, A. (2017).Permukaan Resin Komposit. 4, 38–43

Kawai, K., Urano, M. & Ebisu, (2000).S. Effect Of Surface Roughness Of Porcelain On Adhesion Of Bacteria And Their Synthesizing Glucans. J. Prosthet. Dent. 83, 664–667

Moon, J.-D. Et Al. (2015). Effect Of Immersion Into Solutions At Various Ph On The Color Stability Of Composite Resins With Different Shades. Restor. Dent. Endod. 40, 270

Nabilla, M. A., Usri, K. & Djustiana, N. (2021).Survei Penggunaan Amalgam Oleh Dokter Gigi Di Kota Bandung Setelah Pelarangan Penggunaan Alat Kesehatan Mengandung Merkuri. J. Kesehat. Gigi Dan Mulut 3, 15–24

Nuari, S. (2019). Pengaruh Larutan Kopi Arabika Terhadap Kekuatan Tekan Resin Komposit Nanofiller. 31–34 At

Pardosi, F. M., Indraswari, D. A., Batubara, L. & Hardini, N. (2021).Pengaruh Perendaman Kopi Robusta Dan Arabika Terhadap Kekerasan Resin Komposit Nanofiller. E-Gigi 9, 118–123

Prasetyo, L. S., Harniati, E. D. & Budiono, B. (2023).Pengaruh Ph Asam Terhadap Kekuatan Mekanik Fiber E-Glass: Systematic Review. Indones. J. Dent. 2, 5

Sakaguchi, R.L., Powers, J. . (2012). Craig’s Restorative Dental Materials, 13th Edition. British Dental Journal Vol. 213

Sakaguchi, R.L., Powers, J. . (2019).Craig’s Restorative Dental Materials, Fourteenth Edition. American Journal Of Orthodontics Vol. 71

Sitanggang, P., Tambunan, E. & Wuisan, J. (2015). Uji Kekerasan Komposit Terhadap Rendaman Buah Jeruk Nipis (Citrus Aurantifolia). E-Gigi 3,

Syahrial, A. A., Rahmadi, P. & Putri, D. K. T. (2016).Perbedaan Kekerasan Permukaan Gigi Akibat Lama Perendaman Dengan Jus Jeruk (Citrus Sinensis. Osb) Secara In Vitro. Dentino (Jur. Ked. Gigi) 1, 1–5

Tandrayuana, F. A., Prasetyo, E. A. & Setyabudi, S. A. (2017).Perbedaan Lama Perendaman Air Perasan Jeruk Nipis (Citrus Aurantifolia Swingle) Terhadap Kekasaran Permukaan Resin Komposit Nanohybrid. Conserv. Dent. J. 7, 43

Yunus, Y. N. D. And Y. N. (2020).Pengaruh Perendaman Jeruk Nipis (Citrus Aurantifolia) Terhadap Kekerasan Permukaan Resin Komposit Nanofiller. Sarjana Thesis, Universitas Brawijaya. Kaos Gl Dergisi Vol. 8

Zakiyah, D., Effendy, R. & Prasetyo, E. A. (2019).The Effect Of Glycerin On The Surface Hardness And Roughness Of Nanofill Composite. Conserv. Dent. J. 8, 104

Zhao, Y. Et Al. (2019). Corrosion Behaviour Of Low Dielectric Glass Fibres In Hydrochloric Acid. J. Non. Cryst. Solids 511, 212–218